T 30 SW

T 30 SW

T 30 SW is a polypropylene hofnopolymer for the production of film yam and monofilament T 30 SW features outstanding proceeeability and low water carry-over properties.
T 30 SW Is particularly suitable for the high speed extrusion of film yam for industrial fabrics, heavy duty bags, ropes and twines. The product is also suitable for the production of water-quenched blown film and monofilament.


PROPERTIES METHOD (b) UNIT TYPICAL VALUE (a)
Melt Flow Rate (230 °C . 16 kg) (1) ASTM D 1238L Dg/min 3,2
Density (2) ASTM D 1505 g/cm3 0.9
Flexural modulus (3) ASTM D 790
N/mm2
1550
Tensile strength yield (3) ASTM D 638
N/mm2
35
Elongation at yield (3) ASTM D 638
%
12
Izod Impact Strength (notched) at 23°C
at -20°C (3)
ASTM D 256
J/m
55
Rockwell Hardness (3) ASTM D 785
R scale
102
Vicat softening point (3) ASTM D 1525
°C
156
HDT (0.46 N/mm2) (3) ASTM D 648
°C
94
Accelerated oven ageing air (forced circulation) at 150°C ASTM D 3012
hours
360

T 30 SW is suitable for food contact.

1) Measured at230°C under a load of 2.160 kg, with a standard nozzle having a diameter of 2.095 mm.
2)
Average nominal value referred to a tensile injection mo’;ded specimen, type I (ASTM D 638).
3)
Typical mechanical property values measured on standard specimens, injection moulded under conditions designed to minimise orientation and in-moulded stresses and in line with the conditions generaIy used by industrial converters. Specimens are concitioned at room temperature (ASTM D618 - Procedure A).
4)
The compositon of the product complies with the regulations in force in major European countries concerning polypropylene resins for use in food contact applications. Further details can be supplied on request.