X 30 S

X 30 S

X 30 S is a homopolymer particularly suited for the extrusion of cast and water quenched blown film. X 30 S is formulated with a general purpose stabilisation package and does not contain any slip or antiblocking agents.
X 30 S exhibits excellent pcocessability and outstanding optical properties. This makes X 30 S particularly suitable for film for packaging food-stuffs such as pasta, snacks, biscuits, bakery products and confectionery.
Other applications include film for packaging for flowers, books, stationery, blankets, shirts, knitwear and hosiery.
X 30 S is also very appropriate for the extrusion of small pipes and drinking straws.
X 30 S can be used for lamination with polyester, polyamide and aluminium for packaging of snacks, crisps, sweets, coffee, meat products and pre-cooked foods.
In these applications, X 30 S gives an excellent high gloss finish in laminates and exhibits good printability after Corona treatment.
X 30 S can also be coextruded with and VALTEC heterophasic copolymer grades to produce high gloss finishes on blow moulded pigmented bottles and coextruded sheet.


PROPERTIES
METHOD (b) UNIT TYPICAL VALUE (a)
Physical properties
Melt flow rate (230 °C, 2.16 kg)
Density
ISO 1133
ISO 1183
dg / min
g/cm3
9
0.9
Mechanical properties
Flexural modulus
Tensile strength yield
Elongation at yield
Izod Impact Strength (notched) at 23°C
Hardness Shore D
ISO 178
ISO R 527
ISO R 527 
ISO 180
ISO 868
N/mm2
N/mm2
%
kJ/m2
points
1500
34
13
4
71
Thermal properties
Vicat softening point (9.8 N)
H.D.T. (0.46 Mpa)
Accelerated oven ageing in air
(forced circulation) at 150 °C
ISO 306/A
ISO 75/B
ISO 4577
°C
°C
hours
155
115
360
Optical Properties
Haze
Gloss (45°C)
MTM 17031
MTM 17021
%
%
1
85

a) Values shown are averages and are not to be considered as product specification These values may shift slightly as additional data are accumlsted.
b) ISO test methods are the lates under the societys current procedures. All specimens are prepared by injection moulding.