599 RCXP

599 RCXP

599 RCXP is a medium modified random copolymer for the production of cast and blown film with a reduced blooming effect.
599 RCXP is formulated with slip” and antiblocking agents and exhibits very low blooming properties.
599 RCXP offers easy processability on both cast and water-quenched blown film lines.
The mechanical properties of film made with 599 RCXP are outstanding and the optical characteristics are superior to films made with conventional random copolymers.
The seal initiation temperature is about 130°C and the blooming effect is minimal.
Because of the good heat weldability. 599 RCXP is suitable for monolayer film as well as for sealing layer in coextruded films or laminated structures (e.g. with BOPP, PA, polyester or aluminium).
Films produced with 599 RCXP are particularly suited for the packaging of foodstuffs and textiles and for the production of stationery folders.


PROPERTIES
METHOD (b) UNIT TYPICAL VALUE (a)
Physical properties
Melt flow rate (230 °C, 2.16 kg)
Density
ISO 1133
ISO 1183
dg / min
g/cm3
9
0,9
Mechanical properties
Flexural modulus
Tensile strength yield
Elongation at yield
Izod Impact Strength (notched) at 23°C
Hardness Shore D
ISO 178
ISO R 527
ISO R 527 
ISO 180
ISO 868
N/mm2
N/mm2
%
kJ/m2
points
950
25
13
4
65
Thermal properties
Vicat softening point (9.8 N)
H.D.T. (0.46 Mpa)
Accelerated oven ageing in air
(forced circulation) at 150 °C
ISO 306/A
ISO 75/B
ISO 4577
°C
°C
hours
135
82
360
Optical Properties
Haze
Gloss (45°C)
MTM 17031
MTM 17021
%
%
1,8
85

a) Values shown are averages and are not to be considered as product specification These values may shift slightly as additional data are accumlsted.
b) ISO test methods are the lates under the societys current procedures. All specimens are prepared by injection moulding.